EN 10083-2: 06 Standard
W.NR.: 1.1151/C22E
Non-Alloy Special Steel
Heat analysis according to the EN 10083-2: 06 standard
| C % | Si % | Mn % | P % | S % | Cr % | Ni % | Mo % | Cr+Mo+Ni % | |
| From | 0,17 | – | 0,40 | – | – | – | – | – | – |
| To | 0,24 | 0,40 | 0,70 | 0,030 | 0,035 | 0,40 | 0,40 | 0,10 | 0,63 |
According to the UNI 10233-3 standard
| Thickness mm | Cold Drawn | ||
| ( +C ) | |||
| Rp0,2 minimum | Rm minimum | A5 % | |
| (MPa) | (MPa) | Values | |
| ≤5 | 450 | 570 | 5 |
| >5≤10 | 400 | 520 | 6 |
| >10≤16 | 340 | 520 | 7 |
| >16≤25 | 310 | 520 | 8 |
| >25≤40 | 265 | 460 | 9 |
| >40≤100 | 205 | 380 | 11 |
| >100 | 205 | 380 | 11 |
*Delivery condition: as rolled.
Semi-hard, tough carbon-steel, easily machinable by cold-strain.
Weldability:
Easily weldable.
Hardenability:
Extremely low hardenability, used above all for pieces of small section and when deformations due to water-quenching are allowed.
Notes:
CORRESPONDENCE WITH OTHER STANDARDS (purely as an indication):
| DIN 17200 | AFNOR 35-551 |
| CK22 | XC18 |